| Product Overview | It is a two-component material mainly composed of aliphatic polyaspartic ester polyurea resin as the film-forming substance, with excellent corrosion resistance, color change resistance, and weather resistance. The product has high solidity and low viscosity, good leveling performance, and meets environmental protection requirements; Excellent construction performance, can be applied using any construction coating method, and can be cured in a low-temperature 0 ° C environment in winter; The coating is flexible, wear-resistant, impact resistant, and has excellent chemical resistance, making it an ideal weather resistant and environmentally friendly floor coating material |
| Technical Parameter： |
| project | A | b
|
appearance
| Colorless viscous liquid | Color adjustable |
| Ratio（g/cm3） | 1.04
| 1.50 |
| Viscosity | 40-60 | 100-200 |
| Solid Content | 65 | 88 |
| Mixing ratio (weight ratio) | 1
| 1 |
| surface drying time | 1 |
|
Usage periodMin（25℃）
| 40 |
|
| Theoretical coating rate (film thickness below the table) | 0.15kg/m100m |
|
|
project
| Testing standards | result |
| Hardness |
| 2H |
| Adhesion (MPa) Metal substrate | HG/T 3831-2006 | 9.3
|
| Adhesion (MPa) of concrete substrate | HG/T 3831-2006 | 2.8
|
| Impermeability |
| 2.1MPa |
| Bending test (cylindrical shaft) |
| ≤1mm |
| wear resistance（750g/500r）mg | HG/T 3831-2006 | 5 |
| Impact Strengthkg*cm | GB/T 1732 | 50 |
| Weather resistance, artificial accelerated aging 2000h | GB/T 14522-1993 | Loss of luster<1，pulverization<1 |
|
| Product Features | Low viscosity, good leveling performance, tough and dense coating, full and bright, with bright colors; Strong adhesion to the grassroots and good compatibility with materials such as polyurethane and epoxy; Excellent wear resistance and impact resistance |
| Good waterproof and moisture-proof performance; Excellent resistance to chemical media, such as acid, breakage, salt, etc; This product does not contain benzene solvents or harmful heavy metals, and is environmentally friendly |
| Not prone to discoloration, yellowing, powdering, and aging, with excellent weather resistance and color retention |
| Product corrosion resistance performance | project | result
|
| Acid resistance30%H，SO，10%HCI，240h | No corrosion, no discoloration, no detachment |
| Alkali30%Naoh,240h | No corrosion, no discoloration, no detachment |
| salt tolerance30g/L，240h | No corrosion, no discoloration, no detachment |
| Salt spray resistance 1500h | No corrosion, no discoloration, no detachment |
| Oil resistant 0 # diesel, crude oil | No corrosion, no discoloration, no detachment |
| Water resistance for 48 hours | No bubbles, wrinkles, discoloration, or detachment |
| Construction grassroots treatmen-- |
| Metal surface： | Suggest sandblasting for rust removal to achieve Sa2.5 level according to ISO8501-1 or GB8923 standards |
| Concrete surface： | Achieve a sturdy, dense, smooth, clean, and dry state. There should be no sanding, rusting, cracking, honeycomb or rough surface. Usually requires putty repair |
| wood surface： | Clean, dry, without burrs, fragments, and loose fragments |
precautions
| Before use, stir component B thoroughly and evenly |
| Mix according to the required ratio, mix as much as needed, stir evenly before use, and use the prepared materials within 1 hour |
| After painting, the raw materials inside the packaging bucket must be tightly sealed to prevent moisture absorption |
| During the construction process, keep it dry and clean, and strictly prohibit contact with water, alcohol, acid, alkali, etc |