| application | A type of aliphatic polyisocyanate. Colorless to slightly yellow transparent liquid at room temperature |
| This product belongs to isocyanurate esters |
| equivalent~210 |
| density（25C）~1.08 g/cm3 |
| performance index | project | index
|
| Mass fraction of isocyanate (- NCO) | 19.00~21.00 |
| Viscosity (25 ° C) | 200~700mPa.s |
| chroma | ≤ 40 (platinum cobalt color code) |
| Packaging specifications | 20kg iron drum, 60kg iron drum, 220kg iron drum |
| Customized packaging can be made according to customer needs |
| Storage (use) precautions | Store in a cool, dry, and well ventilated warehouse. Stay away from sources of fire and heat. Keep the container sealed. It should be stored separately from oxidants, acids, bases, alcohols, and edible chemicals, and avoid mixing storage |
| Esters, ketones, aromatic solvents such as ethyl acetate, butyl acetate, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, toluene, xylene, etc. can be used for dilution. Generally, it has good miscibility with the above-mentioned solvents, but the storage stability of the prepared solution must be tested. An urethane grade solvent (with a water content of less than 0.05% and no active groups such as hydroxyl or amino groups) should be used |
| Fatty hydrocarbons are not suitable as solvents |
| The product should not be diluted to a solid content of less than 40%. Solutions with low base material content may become turbid and precipitate after long-term storage |
| compatibility | It can generally be used with aliphatic polyisocyanates, aromatic polyisocyanates, polyether polyols, and polyacrylic esters, but the compatibility of the prepared solution needs to be tested |
| quality guarantee period | This product is sensitive to moisture and is recommended to be stored in its original sealed container under cool and dry conditions at 0-30 ° C. High temperature storage will lead to an increase in viscosity and color number. With proper storage conditions, the product has a shelf life of at least 6 months |