| application | This product is a solvent-free resin with secondary amino groups that can react with - NCO |
| Product Features | This product has excellent compatibility with most hydroxy acrylic resins, CAB, etc |
| High solid and low viscosity, can be made into environmentally friendly coatings with high solid content and low viscosity (construction solid content can reach 100%) |
| ABS, PC, PVC and other plastics, as well as various metals, have excellent adhesion |
| The coating has excellent fullness, leveling performance, and gloss |
| The paint film also has excellent weather resistance, water resistance, solvent resistance, acid and alkali resistance, salt spray resistance and other properties |
| High hardness (up to 2H); Outstanding wear resistance [wear loss<20mg (500r/750g)] |
| application | Widely applicable in the field of automotive paint, it can significantly improve the fullness, gloss, hardness of the paint film and accelerate the drying process |
| It can be widely used in the fields of high-end industrial paint and wood paint, especially for occasions that require high hardness and high wear resistance |
| Can be used as a coating and topcoat for heavy and light anti-corrosion fields such as steel structures and oil pipelines |
| Can be used to prepare high-end solid wood color brushes |
| In the field of fan blade coatings, such as fan blade coating, putty, and topcoat, etc |
| Due to its 100% solid content, low viscosity, good wettability, and wide compatibility, this resin can be widely used for grinding high concentration color pastes, especially suitable for grinding high concentration general-purpose color pastes in the field of automotive repair paint. (The white paste ground with this resin can reach 100% solid content, and the titanium dioxide content can reach about 70%; it is very suitable for grinding high pigment carbon black, with better blackness than ordinary acrylic acid.) |
| performance index | Relative molecular weight -578 |
| Appearance - Slightly yellow transparent liquid |
| Solid content (%) -95 ± 2 |
| NH equivalent (g/mol) -------290 |
| Equivalent to OH content (%) -5.86 |
| Viscosity (MPa. s/25 ° C) --850 ± 1250 |
| Relative density (relative water/25 ℃) -1.05 ± 0.02 |
| Packaging specifications and shelf life | Iron drum packaging, 5kg/drum, 200kg/drum, 10kg/drum |
| 12 months |