Detailed introduction
application | This product is a solvent-free resin with secondary amino groups that can react with - NCO | |||
| Product Features | High solid and low viscosity, can be made into environmentally friendly coatings with high solid content and low viscosity (construction solid content can reach 100%) | |||
| The coating has excellent fullness, leveling performance, and gloss | ||||
| The paint film also has excellent weather resistance, water resistance, solvent resistance, acid and alkali resistance, salt spray resistance and other properties | ||||
| High hardness (up to 2H); Outstanding wear resistance [wear loss. 20mg (500r/750g)] | ||||
| ABS, PC, PVC and other plastics, as well as various metals, have excellent adhesion | ||||
| This product has excellent compatibility with most hydroxy acrylic resins, CAB, etc | ||||
| application | Widely applicable in the field of automotive paint, it can significantly improve the fullness, gloss, hardness of the paint film and accelerate the drying process | |||
| It can be widely used in the fields of high-end industrial paint and wood paint, especially for occasions that require high hardness and high wear resistance | ||||
| Can be used as a coating and topcoat for heavy and light anti-corrosion fields such as steel structures and oil pipelines | ||||
| Can be used to prepare high-end solid wood color brushes | ||||
| In the field of fan blade coatings, such as fan blade coating, putty, and topcoat, etc | ||||
| Due to its 100% solid content, low viscosity, good wettability, and wide compatibility, this resin can be widely used for grinding high concentration color pastes, especially suitable for grinding high concentration general-purpose color pastes in the field of automotive repair paint. (The white paste ground with this resin can reach 100% solid content, and the titanium dioxide content can reach about 70%; it is very suitable for grinding high pigment carbon black, with better blackness than ordinary acrylic acid.) | ||||
| performance index | Relative molecular weight -554 | |||
| Appearance - Slightly yellow transparent liquid | ||||
| Solid content (%)------97±2 | ||||
| NH equivalent (g/mol) ------275 | ||||
| Equivalent to OH content (%) ------6 | ||||
| Viscosity (MPa. s/25 ° C) -----900-1300 | ||||
| Flash point (℃)-----90-95 | ||||
| Relative density (relative water/25 ℃)----1.06±0.02 | ||||
| Packaging specifications and shelf life | Iron drum packaging, 5kg/drum, 200kg/drum, 10kg/drum | |||
| 12 months | ||||