Detailed introduction
Putty layer
| Scope of application: | A four component high-performance polyurethane composite flooring material, which combines almost all the advantages of organic polymers and inorganic concrete, is particularly suitable for use in extreme industrial environments such as food hygiene, chemical corrosion, high temperature and humidity, water wet and slippery, low temperature freezing, and heavy load and strong impact. Water based green, low-carbon and environmentally friendly | ||
| Coating characteristics: | Strong impact resistance, high wear resistance, and a service life of up to 20-30 years | ||
| Resistant to high and low temperatures of -40~130 ° C | |||
| Excellent water vapor permeation function | |||
| Extremely low VOC emissions | |||
| Rapid curing performance | |||
| TECHNICAL INDEX | Drying time - Table drying：≤4H | ||
| Drying time - practical：≤24H | |||
| Hardness：≥2H | |||
| impact resistance（500g steel ball）:50g.cm | |||
| wear resistance（750g/500r）：≤0.03g | |||
| Compressive strength: ≤ Grade 1 | |||
| Resistant to 60% sulfuric acid: no significant change after 7 days | |||
| 31% salt tolerance: no significant change after 7 days | |||
| Resistant to 10% nitric acid: no significant change after 7 days | |||
| Resistant to 10% acetic acid: no significant change after 7 days | |||
| Resistant to 20% sodium oxide gas: no significant change after 7 days | |||
| Resistant to 10% hydrofluoric acid: no significant change for 7 days | |||
| Resistant to gasoline 120 #: No significant change after 7 days | |||
| Construction procedures | construction method | Main materials - auxiliary materials | Reference amount |
| Plain ground | Do a good job in waterproofing treatment | ||
| undercoat | Scrape and apply epoxy primer | DS-30# | About 0.15kg/m ² |
| screed | Scrape the mortar layer with medium coating and quartz sand | DS-400- Quartz sand | 0.25-0.75kg/m² |
| Apply putty layer with intermediate coating and scraping | DS-400 | 0.15kg/m²一遍 | |
| Carbon black layer | Scrape and roll the conductive carbon black coating once | DS-810 | 0.15-0.18kg/m² |
| copper foil | Lay copper foil horizontally and vertically at intervals of 1.5-2m (seal the copper foil with Dongsheng DS-401) | DS-900 | 0.25-3kg/m² |
| top coat | Roll coating anti-static flat topcoat | DS-401 | 0.12kg/m2 |
| Electrostatic wear-resistant layer | Scrape and roll apply polyurethane anti-static and wear-resistant topcoat at the same time | ||
| Construction procedures | Coating thickness: generally 1mm-3mm. If it exceeds 2mm, it needs to be sandblasted | ||
| Personnel can only enter after 24 hours of construction completion, and heavy pressure can only be applied after 72 hours. (Based on 25 * C, the low-temperature opening time needs to be moderately extended) | |||