| Scope of application: | Suitable for high environmental protection and relatively humid floor environments, such as food factories, electronics factories, pharmaceutical factories, cosmetics factories, paper mills, logistics warehouses, basements, home decoration, tooling walls, color changing walls, and other areas that require clean floors |
| Coating characteristics: | Environmentally friendly and easy to construct |
| Resistant to general chemical corrosion |
| Beautiful and smooth, with excellent texture |
| Excellent bonding strength |
| TECHNICAL INDEX | Drying time - surface drying: ≤ 1H |
| Drying time - practical: ≤ 14H |
| Pencil hardness: ≥ 1H |
| Impact resistance (500g steel ball): through cm |
| Wear resistance (750g/500r): ≤ 0.02g |
| Adhesive strength: ≥ Level 2 |
| Resistant to 3% saline solution: no significant change for 7 days |
| Water resistance: No significant change after 7 days |
| Resistant to 20% sodium oxide gas: no significant change after 7 days |
| Resistant to gasoline 120 #: No significant change after 7 days |
| Construction procedures | construction method | Main materials - auxiliary materials | Reference amount |
| Plain ground | Do a good job in waterproofing treatment |
|
|
| undercoat | Roll on water-based epoxy base oil | DS-606 | About 0.15kg/m ² |
| screed | Waterborne epoxy intermediate coating mixed with quartz sand scraping coating | DS-608- Quartz sand | 0.25-0.6kg/m²
|
| Putty layer | Waterborne epoxy intermediate coating, adjusting weight, calcium powder, scraping putty layer | DS-608-- Heavy Calcium Powder | 0.1kg/m2 once |
| top coat | Rolling or spraying water-based polyurethane topcoat | DS-603 | 0.12/m2 |
| After completion, the overall floor will be bright and clean, with uniform color and no hollowing |
|
| Construction procedures | Coating thickness: generally 1mm-3mm. If it exceeds 2mm, it needs to be sandblasted |
| Personnel can only enter after 24 hours of construction completion, and heavy pressure can only be applied after 72 hours. (Based on 25 * C, the low-temperature opening time needs to be moderately extended) |