| Scope of application: | Industrial plants, offices, warehouses, food factories, etc. require pressure resistance, seamless cleanliness, dust-proof areas, and repair of old floors |
| Coating characteristics: | Pressure resistance, impact resistance, and general chemical corrosion resistance |
| Fast construction, environmentally friendly, seamless dust-proof, easy to clean |
| Colorful, beautiful and bright |
| Good wear resistance and long service life |
| TECHNICAL INDEX | Drying time - surface drying: ≤ 4H |
| Drying time - practical: ≤ 24 hours |
| Pencil hardness: ≥ 2H |
| Impact resistance (500g steel ball): through g.cm |
| Wear resistance (750g/500r): ≤ 0.03 |
| Durability (grid method): Level 1 |
| Resistant to 3% saline solution: no significant change for 7 days |
| Resistant to 10% sulfuric acid: no significant change after 7 days |
| Resistant to 20% sodium oxide gas: no significant change after 7 days |
| Construction procedures | construction method | Main materials - auxiliary materials | Reference amount |
| Plain ground | Do a good job in waterproofing treatment |
|
|
| undercoat | Roll coated epoxy primer | DS-30# | About 0.15kg/m ² |
| screed | Add quartz sand to scrape and apply epoxy intermediate coating | DS-400- Quartz sand | 0.25-0.7kg/m²
|
| Putty layer | Scrape and apply putty layer | DS-400 | 0.1kg/m2 once |
| top coat | Roll coated epoxy topcoat layer | DS-145 | 0.15-0.18kg/m²
|
| After completion, the overall floor will be bright and clean, with uniform color and no hollowing |
|
| Construction procedures | Coating thickness: generally 1mm-3mm. If it exceeds 2mm, it needs to be sandblasted |
| Personnel can only enter after 24 hours of construction completion, and heavy pressure can only be applied after 72 hours. (Based on 25 * C, the low-temperature opening time needs to be moderately extended) |