| product overview | Prepared from epoxy resin, iron red powder, pigments, fillers, additives, solvents, amine curing agents, etc |
| Performance and Application | The paint film has good water resistance and salt spray resistance; Good resistance to chemical media and air permeability. Good rust prevention effect. Applied to rust prevention on the surface of steel structures |
| Physical parameters | Density -1.3-1.4g/ml |
| Theoretical dosage: 5-6 ㎡/kg (calculated based on a dry film thickness of 40um) |
| Salt water resistance - no foaming or peeling for ≥ 48 hours |
| Proportion - Component A: Component B=9.5:1 |
| Drying time - surface drying ≤ 2 hours; Practical work ≤ 24 hours |
| Impact strength -50kg.cm |
| Adhesion force ---- ≤ 1 (grid method) |
| Maturity period -10-15 minutes |
| Probationary period -2 hours (25 ℃) |
| Color - Iron Red |
| Interval time for recoating | One coat per day, it is recommended to apply two to three coats of paint |
| Front supporting paint | Epoxy, chlorinated rubber, polyurethane, acrylic and other topcoats |
| Substrate temperature | 3 ° C above dew point |
| instructions | 1. The surface of steel workpieces must be degreased and cleaned, and sandblasting must comply with Swedish standard Sa2.5 level |
| 2. The components A and B should be strictly mixed according to the prescribed ratio, and appropriate diluents should be added to adjust the construction viscosity to the appropriate level. It is recommended to adjust the construction viscosity for 20-25 seconds (25 ℃), mix thoroughly and filter with a 60-80 mesh sieve, and let it stand for 10-15 minutes before construction |
| 3. After mixing two components, they should be used up within the specified time (4 hours at 30 ℃ and 6 hours at 20 ℃) |
| 4. For special areas such as corners, welds, cutting, and inadequate spraying, 1-2 coats of this coating should be applied before spraying, followed by extensive spraying to ensure the thickness of the paint film in each area |
| 5. Ensure the required paint film thickness for corrosion inspection. If the thickness requirement cannot be met, three or four coats of spraying are required. Because sufficient thickness of anti rust paint film is the guarantee for rust and corrosion prevention of steel structures |
| 6. Spray coating (recommended spray pressure 0.4-0.5 megapascals), roller coating, brush coating |
| 7. To ensure quality, please use HX062 epoxy diluent |
| Storage period | Sealed storage in a cool and dry place, with a shelf life of 12 months. If it exceeds the shelf life and passes inspection, it can still be used |