| Material Description | KED-M001 water-based ceramic polymer topcoat has excellent weather resistance. It is a material based on silica sol organosilane and composite with rare earth, aluminum oxide, and titanium oxide, which improves the brittleness of pure inorganic coatings and retains the high weather resistance, wear resistance, temperature resistance, and self-cleaning properties of inorganic ceramics. It is a long-term environmentally friendly coating mainly used as a topcoat to improve weather resistance and corrosion resistance |
| main features | Simple construction, can be sprayed or brushed with multiple construction methods |
| Environmentally friendly, no heavy metal leaching |
| Has excellent weather resistance, superior to fluorocarbon paint, and a long service life |
| Excellent wear resistance, outstanding wind and sand erosion resistance, superior to fluorocarbon paint |
| For Class A non combustible materials |
| Good self-cleaning performance |
| Temperature resistance 260 ° C |
Comparison of different performance topcoats
|
| category | KED water-based ceramic polymer topcoat | Fluorocarbon paint | Inorganic zinc rich primer | Ceramic |
| environmentally | environment protection | VOC emissions and pollution | VOC emissions and pollution | High energy consumption |
| Usage performance | Convenient construction | Convenient construction | Convenient construction | Construction can only be carried out within the factory |
| hardness | 4-9H
| F-2H | 2H | 3-6H |
| Weather resistance | >4000h，semi-permanent | 3000h | 1000h | semi-permanent |
| flammability | A-class non combustible | B-class flame retardant, smoking | combustible | A-class non combustible |
| self-cleaning property | good | better | general | better |
| wear resistance | More than 15 times that of fluorocarbon | better | general | good |
| Basic parameters | Usage ratio: A: B=7:3 |
| Dry conditions | 1. Bake completely dry, 150 * C * 20 minutes |
| 2. Or cure at room temperature, dry for 1 hour (25 ° C) |
| 3. It takes seven days (25 ° C) to reach the final strength |
| Volume solid content: 45-50% |
| Specific gravity: 1-1.2g/cm3 |
| Theoretical dosage without waste: 50g/(dry film 20 microns) |
| Viscosity: FORD 4 #, 10-14 seconds (20 ° C) |
| Flash point: 36 ° C |
| Recommended film thickness: 20-40 microns |
| Shelf life: sealed away from light, before mixing: 12 months from the date of manufacture; After mixing, store in a sealed container for 2-3 days |
| application area | Protection of military vehicles, military facilities, ships, etc |
| Protection for building steel structures, wind turbine towers, bridges, metal equipment, etc |
| Ultra wear-resistant ground and wear-resistant protection |