| Product composition | A two-component coating composed of chlorosulfonated polyethylene resin, modified epoxy resin, anti-corrosion pigments, fillers, additives, solvents, etc |
| Performance and Usage | Dry quickly; High hardness; Strong adhesion, good mechanical performance, excellent protection performance, and outstanding three proof performance; Good supporting performance |
| Used for steel structures, pipelines, storage tanks, machinery and other equipment, as well as for anti-corrosion coating in chemical plants, fertilizer plants, power plants, refineries, paper mills, and sewage treatment plants |
| Technical Parameter | Non volatile matter - ≥ 30% |
| Composite coating resistant to 30% NaOH (30d) - no foaming, no rusting, no peeling |
| Composite coating resistant to 30% H2SO4 (30d) - no foaming, no rusting, no peeling |
| Composite coating resistant to 30% NaCl (30d) - no foaming, no rusting, no peeling |
| Salt water resistance (3% NaCl, 4d) - no foaming, no rusting, no peeling, slight color loss allowed |
| Color and appearance - The color tone is unpredictable, and the paint film is smooth and even |
Specific gravity - about 1.28kg/L
|
| Impact strength -50kg.cm |
| Flexibility - ≤ 1mm |
| Adhesion (circle drawing method) ------- ≤ Level 2 |
| Drying time - surface drying ≤ 0.5 hours; Practical work ≤ 24 hours (under 25 ℃ conditions) |
| Construction reference | 1. Surface treatment: Sandblasting and shot blasting to remove oxide scale, rust, and oil stains, reaching Sa2.5 or St3 levels |
| 2. Substrate temperature: 3 ℃ above dew point |
| 3. Painting methods: brush coating, roller coating, spray coating |
| 4. Diluent: Special diluent for chlorosulfonated polyethylene paint adjusted to appropriate viscosity for use |
| 5. Coating thickness: Generally, two coats are recommended, with a dry film thickness of 70 µ m |
| 6. Theoretical dosage: approximately 4.8 ㎡/kg (based on a dry film of 30 µ m) |
| 7. Re coating interval time: 6 hours at 25 ℃, with no maximum limit |
| 8. Rear supporting paint: chlorosulfonated polyethylene topcoat |
| safety rules | The construction site should have good ventilation facilities |
| Construction personnel should wear protective equipment such as masks, glasses, gloves, etc. to avoid skin contact and inhalation of paint mist and solvents |
| Smoking is strictly prohibited on the construction site, and all sources of fire must be isolated |
| Storage period | Sealed storage in a cool and dry place, with a shelf life of 12 months. If it exceeds the shelf life and passes inspection, it can still be used |